ExplainAfter braid of alkali free glass fiber through high temperature treated surface by silicone copolymerization tree
High temperature resistance (200 c)
High pressure resistant FSG-1 1200V, FSG-2 1500V
FSG-3 2500V, FSG-4 4000V
Flame retardant UL224 VW-1
Good mechanical properties
Good insulation performance
Good softness
Through the UL argument
application
It is widely used in H insulation motor, household electrical insulation, electrical insulation and so on.
performance | index |
Bending property after heating | The coating has no visible cracking or exfoliation, and the original color is obviously visible. The test temperature is 260 + 5 C, 48 + 1 hours. |
Flexural properties at low temperature | The coating has no visible cracking or exfoliation, and the original color is obviously visible. Test temperature |
Slow ductility of flame | At the maximum of 60 seconds, the flag of any one of the three tests should not be burned, and the burning or burning particles should not ignite the cotton. |
Temperature index of 20000 hours thermal life | 200℃ |
Standard diameter mm | Tolerance of inner diameter mm | Wall thickness mm | Packing | |
Rice / roll | Rice / disc | |||
0.5 | +0.1 | 0.18 | 100 | 1000 |
0.8 | +0.1 | 0.18 | 100 | 1000 |
1.0 | +0.1 | 0.18 | 100 | 1000 |
1.5 | +0.2 | 0.18 | 100 | 1000 |
2.0 | +0.2 | 0.18 | 100 | 600 |
2.5 | +0.2 | 0.18 | 100 | 500 |
3.0 | +0.3 | 0.23 | 100 | 400 |
3.5 | +0.3 | 0.23 | 100 | 200 |
4.0 | +0.3 | 0.23 | 100 | 200 |
4.5 | +0.3 | 0.28 | 100 | 200 |
5.0 | +0.4 | 0.28 | 100 | 200 |
5.5 | +0.4 | 0.28 | 100 | 200 |
6.0 | +0.4 | 0.32 | 100 | 200 |
7.0 | +0.6 | 0.32 | 100 | 100 |
8.0 | +0.6 | 0.32 | 50 | 100 |
9.0 | +0.6 | 0.32 | 50 | 100 |
10 | +0.8 | 0.52 | 50 | 100 |
11 | +0.8 | 0.52 | 25 | 100 |
12 | +0.8 | 0.52 | 25 | 100 |
13 | +0.8 | 0.52 | 25 |
|
14 | +0.8 | 0.52 | 25 |
|
15 | +0.8 | 0.52 | 25 |
|
16 | +0.8 | 0.52 | 20 |
|
18 | +0.8 | 0.52 | 20 |
|
20 | +0.8 | 0.52 | 20 |
|
25 | +0.8 | 0.52 | 20 |
|
30 | +0.8 | 0.52 | 20 | |